Good for moist and heat resistance in rubber

Unit of Measure

Specifications

Series

N/A 900

Type

N/A 901H2

Unit Size

N/A 50 gm bottle

Units per case

N/A 20

Color

N/A Clear

Gap Fill

N/A 0.004"

Viscosity

N/A 5 cps

Tensile Shear Strength (Steel)

N/A 4000 psi

Temperature Range

N/A -65 ºF to +180 ºF

Set Time (Steel)

N/A 15 s

Bonding Strength to Metal

N/A Good

Bonding Strength to Electroplating

N/A Good

Bonding Strength to Rubber

N/A Good

Bonding Strength to Plastic

N/A Good

Moisture Resistance

N/A Excellent

Set Time(PVC)

N/A 3 s

Set Time (ABS)

N/A 10 s

Set Time (Polycarbonate)

N/A 30 s

Set Time (Chroloprene)

N/A 1 s

Set Time (EPDM)

N/A 1 s

Set Time (Steel)

N/A 15 s

Set Time (Aluminum)

N/A 30 s

Tensile Strength (PVC)

N/A 26 N/mm²

Tensile Strength (ABS)

N/A 13 N/mm²

Tensile Strength (Iron)

N/A 30 N/mm²

Tensile Strength (Aluminum)

N/A 25 N/mm²

Tensile Shearing Strength (Polycarbonate)

N/A 7 N/mm²

Tensile Shearing Strength (Chroloprene)

N/A 0.6 N/mm²

Tensile Shearing Strength (EPDM)

N/A 0.6

Form of Packing (20g)

N/A Good

Tensile Strength

N/A 0.5 x 0.5 x 1.5 inch; bonded area 0.25 sq. inch

Tensile Shear Strength (for plastic and rubber)

N/A 0.1 x 1.0 x 4.0 inch; bonded area 0.5 sq.inch

Tensile Shear Strength (for metal)

N/A 0.064 x 1.0 x 4.0 inch; bonded area 0.5 sq. inch

Bonding Atmosphere

N/A 22 to 24 ºC72 to 75 ºF

Relative Humidity

N/A 58-62%

Testing Methods

N/A ASTM D2095, D3164, and D1002

Before Curing

Appearance (Liquid State)

N/A Colorless and Transparent

Base Monomer (Liquid State)

N/A Ethyl 2-Cyanoacrylate

Viscosity (Liquid State)

N/A 5 cps

Specific Gravity (d20)-(Liquid State)

N/A 1.067

Solubility Parameter

N/A 10-11

After Curing

Appearance (Solid State)

N/A Colorless and Transparent

Specific Gravity (d20)-(Solid State)

N/A 1.214

Hardness (Shore D, 23°C/ 73°F)

N/A 80

Glass Transition Point (Solid State)

N/A 123 ºC253 ºF

Young Modulas (x 109)

N/A 11.4 dynes/cm²

Shrinkage (%)

N/A 12.1

Characteristics of Aron Alpha® Cyanoacrylate Adhesives

Characteristics

N/A
  • Instant Bonding :
    Adhesion is achieved in a few seconds, It is well suited for increasing the efficiency of the manufacturing process.
  • Easy to use:
    Adhesive is single component and heat treatment are not required. Perfect f

Setting Time

N/A

(in seconds for various materials)

Material Setting Times (sec)
  901H2 901H2F 901H3 922H2 903TX
Rigid PVC 3   5 3 5
ABS 10   10 10 10
Natural Rubber 15   30 30 30
Neoprene Rubber 5   5 10 5
Copper 10   10 N/A 10

Bonding Strength (Tensile)

N/A

(Tensile measured in psi for various materials)

Material Tensile Strengths (psi)
  901H2 901H2F 901H3 922H2 903TX
Rigid PVC 3600   3500 3800 2400
Aluminum 2700   2700 2800 1800

Bonding Strength (Shear)

N/A

(Shear measured in psi for various materials)

Material Shear Strengths (psi)
  901H2 901H2F 901H3 922H2 903TX
Natural Rubber 110   110 110 110
Neoprene Rubber 110   110 120 110
EPDM Rubber       190  

Applications

N/A

  • For Wood Work: Suitable for bonding wood. Complete and wide range of adhesive grades available. Suitable for assembling wooden products and repairing. Wooden molds and expensive rare woods.
  • Artificial Marble: For use on artificial marble with various kinds of colors such as transparent, white, black and grey.
  • Color Grades: Able to confirm the coating colors of adhesives.
  • Remover: For use in removing hardened substances and peel off parts of adhesives

Features

N/A

  • Soft and flexible type
  • Excellent resistance to heat and humidity after bonding various rubbers.
  • Low shrinkage property

Storage

N/A

  • Store product in the unopened container in a dry location.

Humidity

  • Avoid moist, humid storage conditions.
  • Fasten cap tightly to avoid exposure to moisture.
  • Store with desiccant.

Temperature

  • Avoid storing at a

Method of Disposal

N/A

  • Expose the adhesives in the containers to moisture and light to let it harden slowly, and to treat it as waste plastics (drastic hardening may result in heating, pay attention to this situation).
  • Please comply with local regulations when dispos

Precaution

N/A

When in contact with Skin

  • Don't peel it off forcibly, instead use warm water or remover to rub it off.

When in contact with Eyes

  • It will damage the eyes to rub the eyes or to use solvents. Must rinse with large amount of water and get medical attention.

Warning

N/A

  • May have an irritating odor, Aron Alpha might irritate eyes, nose and throat. Please maintain proper ventilation it is used in large amounts or for a long period of time. Please wear protective glasses and/or hood shield.
  • In case of absorbing into cloth, Aron Alpha will rapidly polymerize and result in heating. During operation, avoid wearing gloves made of absorbable materials, instead use solvent proof polyethylene gloves.
  • ARON ALPHA is a flammable liquid. Use in a well ventilated area, and keep away from fire.
  • Eye and Skin irritant. Bonds skin instantly. Combustible - keep away from heat and flames.